MIZUNO REPLICATION AND MATERIALS ONLY
-
-
Not so old
-
New
-
For better imagination here we have special plasma processed meshes.
These are different from what is used for Mizuno replication.
They are made of much thicker wire due to technical limitations but have significantly bigger surface area.
-
Next week we will finish Copper plated Nickel meshes. We will see what oxide layer will do there.
-
-
For better imagination here we have special plasma processed meshes.
That surface looks like the Pd electo-plated on Frank Gordon's LEC sample, though your grain structure is coarser and less uniform. Is this using high-temperature plasma spray? The Mizuno mesh looked more like thin-film vapor deposition.
-
There is no Pd yet on this sample. It is high temperature plasma spray.
What we sent to you was very different method of preparation that we are using for over year, more focused on the nano structure at the surface.
-
Daniel_Gはもはやミズノテクノロジーズ株式会社で働いていません。
-
Daniel_Gはもはやミズノテクノロジーズ株式会社で働いていません。
Translated: Daniel G, no longer works for Mizuno Technologies Corporation.
Sorry to hear that.
-
Daniel_Gはもはやミズノテクノロジーズ株式会社で働いていません
ざんねんですね
-
-
Indeed it is very regrettable.
-
Translated: Daniel G, no longer works for Mizuno Technologies Corporation.
Sorry to hear that.
The web site https://mizunotech.com/index.html does not yet reflect this change.
-
The web site https://mizunotech.com/index.html does not yet reflect this change.
barty usually makes changes to the website for Mizuno and Daniel as a favor. He is hard to get in touch with nowadays, so may take a while.
-
magicsound Any progress with the Me356 meshes?
-
Yesterday we finished Copper plated Nickel meshes. Price is significantly lower. We hope to start tests during following week.
I guess Alan will be ready for another test soon.
-
-
Daniel_Gはもはやミズノテクノロジーズ株式会社で働いていません。
Over the past 2 years, on this forum and in public presentations, Daniel_G has made a number of claims regarding excess heat measured from reactors equipped with meshes based on Mizuno's discoveries. Does Mizuno Technologies Corp. support these claims as accurate?
-
Bruce all claims are 100% supported by third parties and that has nothing to do with the situation at MTI. Mizuno and I have a good, positive relationship and I will continue to support and assist him in any way I can.
-
all claims
Daniel
Discussion on this forum is sometimes a little disjointed or even disruptive?
More coherent discussion is in your ICCF24 presentation
I guess the two hypotheses you mentioned are still being tested and will be so for some time..
as well as the investigation of a number of other variables. maybe even samarium...
"
HT 1 "there's an amount of excess heat that is proportional to the surface area of the catalyst"
HT 2 "there's an exponential relationship between the working temperature and the excess heat output
ขอให้โชคดี with PattayaPhysics and PattayaShrimp?
External Content www.youtube.comContent embedded from external sources will not be displayed without your consent.Through the activation of external content, you agree that personal data may be transferred to third party platforms. We have provided more information on this in our privacy policy. -
Bruce all claims are 100% supported by third parties and that has nothing to do with the situation at MTI. Mizuno and I have a good, positive relationship and I will continue to support and assist him in any way I can.
Good to hear.
I continue to encourage you make public the supporting evidence you mention. If you have a good case to make, then make it. Doing so would do nothing but good for your own efforts as well as Mizuno's. Your ICCF-24 presentation
asis a misfire so far as empirical evidence is concerned, and that is a shame. -
Misfire?
-
LENR Partners