Alan Smith , sorry to bother you as you are indeed busy, but as you are back to Ni foam, can you tell us more about the material you have told us is good for separation of the WE and CE, I recall is a mesh but can’t recall the material and if I dreamed or you told us it is covered with a PTFE layer that ensures the isolation and also that it is 0,1 mm thick, is that right?
RE: Frank Gordon / Harper Whitehouse - the LEC -collected papers
The cathode on the left was my first attempt at nickel plating, the nickel deposit on the LHS is way too heavy, so I diluted the 'Watts' plating solution 50/50 to reduce its conductivity and lowered the voltage and current as mentioned above. The result was the electrode on the RHS. The plating is smooth flat and even and well adhered, but still faster than I wanted for co-deposition though. This took 60 minutes the current and voltage are shown below- volts just above the Faraday limit for…